The first ever Canadian five-cent coins were struck by the Royal Mint in London as part of the introductory 1858 coinage of the Province of Canada. The coins were the same size and general composition as the corresponding American coins of the time, so the five-cent coin was based on the half dime. Although the American denomination was introduced as a larger copper-nickel coin in 1866, and the 5 cent silver was retired in 1873, the Canadian five-cent coins remained small and silver until 1922.

All Canadian coins (including five-cent coins) were struck in England at the Royal Mint (no mint mark) and the Birmingham Mint (H mint mark) until 1908, when the Ottawa branch of the Royal Mint opened. With the exception of some 1968 dimes struck at the Philadelphia Mint, all Canadian coins since 1908 have been minted in Canada.

Due to a rise in the price of silver, Canadian coinage was debased from sterling silver (925 fine) to 800 fine in 1920. In 1922, silver was removed entirely from the five-cent coin, replacing it with a coin of roughly the same dimensions and mass as the American nickel. However, unlike the American coin, which was 75% copper and 25% nickel, the Canadian coin was pure nickel, as Canada was the world's largest producer of the metal. This coin has since been known almost universally as the nickel.

The five-cent coin of Newfoundland, on the other hand, remained silver until the end of the Newfoundland coinage in 1947.

The nickel's composition has changed several times, most notably during World War II and the Korean War when nickel was redirected to the war effort, where it was essential for armor production. In the latter part of 1942 and throughout 1943, the coins were minted in tombac, a copper-zinc alloy; in 1944 and 1945, and again from mid-1951 to 1954, coins were made of steel which was plated twice, first with nickel and then chromium. The plating was applied before the blanks were struck, so the edges of these coins are dull or even rusted. The composition was returned to pure nickel after both wars. More recently, in 1982, the same copper-nickel alloy used in the American coin was adopted in the Canadian coin, with the ironic result that the nickel then contained less nickel than any other circulating Canadian coin except the cent. Since late in 2000, the nickel is now generally made with plated steel. Since the plating is now done after the blanks are punched, the edges of the modern coins receive the plating. Portions of the 2001 and 2006 issues were struck in cupro-nickel, and can be identified by the lack of the letter "P" under Queen Elizabeth's portrait, and for their non-magnetic quality.

Starting with the 1942 tombac coins, the nickel was made dodecagonal, presumably to help distinguish it from the cent after it tarnished in circulation. Tombac was removed from the nickel in 1944 (to be replaced by steel, as noted during the Korean war) but the coins in Tombac, steel, or 99.9% nickel all remained twelve-sided until 1963.