Urewe - The Urewe Civilisation in Rwanda and Burundi

The Urewe Civilisation in Rwanda and Burundi

Urewe ceramics are modest in size, measuring from 30 cm up to a maximum of 36 cm in height. Three distinct shapes have been observed: vases, small vases, both closed s-shaped pieces, open-bowls on which stereotyped patterns have been crafted: and bevelling on the rim, hatching on the neck surface for ease of handling, the body decorated with a ribboned pattern of crafted geometrical designs, and a dimple base finish. The decorative markings are adapted to and emphasise the shape of the vase with its 4 components, often seen on the little vase in simplified form. Conversely, these ‘4 component’ patterns are all stuck on the bowl; regardless of its ‘3 components’ shape. One proposed hypothesis suggests the bowl was developed later than the vase. Support for this comes from the identification, in terms of Bantu linguistics, of a new term first appearing around 1000 B.C. meaning “frying pan” probably serving as a clue to a change in cooking techniques reflecting adaptation to a more sedentary lifestyle when Bantu-speaking people began to settle in the Rwanda and Burundi hills.

The ironsmelting furnace associated to these Urewe ceramics comprised a basin filled with fresh green leafy branches and herbs which served as a filter for the slag deposit at the base. Above the basin was a cone-shaped shaft, not unlike a chimney, made by superimposing rolls of damp clay. The decorated furnace, with its fluted patterns on the upper roll and deeply incised criss-cross or s-shaped patterns on the outer surface, may be reminiscent of the rim or neck of the ceramic pottery. Analyses carried out on the ironworking residue have not yet provided data on the efficiency of these furnaces, or whether they were a measure of their technical nature. Iron ore and fuel were readily available. The word “ubutare” meaning “iron” still crops up in many place names. The wooded crown cover was used to produce charcoal. As new wood was always used for this purpose, radiocarbon dating of this material is relatively reliable.