History

Molybdenite—the principal ore from which molybdenum is now extracted—was previously known as molybdena. Molybdena was confused with and often utilized as though it were graphite. Like graphite, molybdenite can be used to blacken a surface or as a solid lubricant. Even when molybdena was distinguishable from graphite, it was still confused with the common lead ore PbS (now called galena); the name comes from Ancient Greek Μόλυβδος molybdos, meaning lead. (The Greek word itself has been proposed as a loanword from Anatolian Luvian and Lydian languages).

Although apparent deliberate alloying of molybdenum with steel in one 14th-century Japanese sword (mfd. ca. 1330) has been reported, that art was never employed widely and was later lost. In in the West in 1754, Bengt Andersson Qvist examined molybdenite and determined that it did not contain lead, and thus was not the same as galena.

By 1778 Swedish chemist Carl Wilhelm Scheele stated firmly that molybdena was (indeed) not galena nor graphite. Instead, Scheele went further and correctly proposed that molybdena was an ore of a distinct new element, named molybdenum for the mineral in which it resided, and from which it might be isolated. Peter Jacob Hjelm successfully isolated molybdenum by using carbon and linseed oil in 1781.

For about a century after its isolation, molybdenum had no industrial use, owing to its relative scarcity, difficulty extracting the pure metal, and the immaturity of appropriate metallurgical techniques. Early molybdenum steel alloys showed great promise in their increased hardness, but efforts to manufacture them on a large scale were hampered by inconsistent results and a tendency toward brittleness and recrystallization. In 1906, William D. Coolidge filed a patent for rendering molybdenum ductile, leading to its use as a heating element for high-temperature furnaces and as a support for tungsten-filament light bulbs; oxide formation and degradation require that molybdenum be physically sealed or held in an inert gas. In 1913, Frank E. Elmore developed a flotation process to recover molybdenite from ores; flotation remains the primary isolation process

During the first World War, demand for molybdenum spiked; it was used both in armor plating and as a substitute for tungsten in high speed steels. Some British tanks were protected by 75 mm (3 in) manganese steel plating, but this proved to be ineffective. The manganese steel plates were replaced with 25 mm (1 in) molybdenum-steel plating allowing for higher speed, greater maneuverability, and better protection. After the war, demand plummeted until metallurgical advances allowed extensive development of peacetime applications. In World War II, molybdenum again saw strategic importance as a substitute for tungsten in steel alloys.

Read more about this topic:  Molybdenum

Famous quotes containing the word history:

    The disadvantage of men not knowing the past is that they do not know the present. History is a hill or high point of vantage, from which alone men see the town in which they live or the age in which they are living.
    Gilbert Keith Chesterton (1874–1936)

    We said that the history of mankind depicts man; in the same way one can maintain that the history of science is science itself.
    Johann Wolfgang Von Goethe (1749–1832)

    The history of the Victorian Age will never be written: we know too much about it.
    Lytton Strachey (1880–1932)