Effect On Cement Properties
In keeping with its high basicity, tricalcium aluminate reacts most strongly with water of all the calcium aluminates, and it is also the most reactive of the Portland clinker phases. Its hydration to phases of the form Ca2AlO3(OH)·nH2O leads to the phenomenon of "flash set" (instantaneous set), and a large amount of heat is generated. To avoid this, Portland-type cements include a small addition of calcium sulfate (typically 4-8%). Sulfate ions in solution lead to the formation of an insoluble layer of ettringite (3CaO·Al2O3·3CaSO4·32H2O) over the surface of the aluminate crystals, passivating them. The aluminate then reacts slowly to form the AFm phase 3CaO·Al2O3·CaSO4·12H2O. These hydrates contribute little to strength development.
Tricalcium aluminate is associated with three important effects that can reduce the durability of concrete:
- heat release, which can cause spontaneous overheating in large masses of concrete. Where necessary, tricalcium aluminate levels are reduced to control this effect.
- sulfate attack, in which sulfate solutions to which the concrete is exposed react with the AFm phase to form ettringite. This reaction is expansive, and can disrupt mature concrete. Where concrete is to be placed in contact with, for example, sulfate-laden ground waters, either a "sulfate-resisting" cement (with low levels of tricalcium aluminate) is used, or slag is added to the cement or to the concrete mix. The slag contributes sufficient aluminium to suppress formation of ettringite.
- delayed ettringite formation, where concrete is cured at temperatures above the decomposition temperature of ettringite (about 65 °C). On cooling, expansive ettringite formation takes place.
Because they are even more basic, the alkali-loaded polymorphs are correspondingly more reactive. Appreciable amounts (>1%) in cement make set control difficult, and the cement becomes excessively hygroscopic. The cement powder flowability is reduced, and air-set lumps tend to form. They withdraw water from gypsum on storage of the cement, leading to false set. For this reason, their formation is avoided wherever possible. It is more energetically favorable for sodium and potassium to form sulfates and chlorides in the kiln, but if insufficient sulfate ion is present, any surplus alkalis congregate in the aluminate phase. The feed and fuel in the kiln system are preferably controlled chemically to keep the sulfate and alkalis in balance. However, this stoichiometry is only maintained if there is substantial surplus oxygen in the kiln atmosphere: if "reducing conditions" set in, then sulfur is lost as SO2, and reactive aluminates start to form. This is readily monitored by tracking the clinker sulfate level on an hour-to-hour basis.
Read more about this topic: Tricalcium Aluminate
Famous quotes containing the words effect, cement and/or properties:
“An actor must communicate his author’s given message—comedy, tragedy, serio- comedy; then comes his unique moment, as he is confronted by the looked-for, yet at times unexpected, reaction of the audience. This split second is his; he is in command of his medium; the effect vanishes into thin air; but that moment has a power all its own and, like power in any form, is stimulating and alluring.”
—Eleanor Robson Belmont (1878–1979)
“It is fair to assume that when women in the past have achieved even a second or third place in the ranks of genius they have shown far more native ability than men have needed to reach the same eminence. Not excused from the more general duties that constitute the cement of society, most women of talent have had but one hand free with which to work out their ideal conceptions.”
—Anna Garlin Spencer (1851–1931)
“A drop of water has the properties of the sea, but cannot exhibit a storm. There is beauty of a concert, as well as of a flute; strength of a host, as well as of a hero.”
—Ralph Waldo Emerson (1803–1882)