Stress Migration is a failure mechanism that often occurs in IC metallization (aluminum, copper). Voids form as result of vacancy migration driven by the hydrostatic stress gradient. Large voids may lead to open circuit or unacceptable resistance increase that impededs the IC performance. Stress Migration is often referred as Stress Voiding, Stress Induced Voiding or SIV.
High temperature processing of copper dual damascene structures leaves the copper with a large tensile stress due to a mismatch in coefficient of thermal expansion of the materials involved. The stress can relax with time through the diffusion of vacancies leading to the formation of voids and ultimately open circuit failures.
Famous quotes containing the word stress:
“While ... we cannot and must not hide our concern for grave world dangers, and while, at the same time, we cannot build walls around ourselves and hide our heads in the sand, we must go forward with all our strength to stress and to strive for international peace. In this effort America must and will protect herself.”
—Franklin D. Roosevelt (1882–1945)