Powder Metallurgy - Isostatic Powder Compacting

Isostatic Powder Compacting

Isostatic powder compacting is a mass-conserving shaping process. Fine metal particles are placed into a flexible mould and then high gas or fluid pressure is applied to the mould. The resulting article is then sintered in a furnace. This increases the strength of the part by bonding the metal particles. This manufacturing process produces very little scrap metal and can be used to make many different shapes. The tolerances that this process can achieve are very precise, ranging from +/- 0.008 inches (0.2 mm) for axial dimensions and +/- 0.020 inches (0.5 mm) for radial dimensions. This is the most efficient type of powder compacting.(The following subcategories are also from this reference.) This operation is generally applicable on small production quantities, as it is more costly to run due to its slow operating speed and the need for expendable tooling.poda

Compacting pressures range from 15,000 psi (100,000 kPa) to 40,000 psi (280,000 kPa) for most metals and approximately 2,000 psi (14,000 kPa) to 10,000 psi (69,000 kPa) for non-metals. The density of isostatic compacted parts is 5% to 10% higher than with other powder metallurgy processes.